Name | N,N'-hexamethylenebis(cinnamylideneamine) |
Synonyms | Diak 3 Aids124957 Diak no. 3 Aids-124957 Dicinnamylidene hexamethylenediamine N,N'-hexamethylenebis(cinnamylideneamine) 1,6-Hexanediamine, N, N'-dicinnamylidene- N1,N6-Bis(3-phenylallylidene)hexane-1,6-diamine N,N'-Bis(3-phenyl-2-propenylidene)-1,6-hexanediamine N,N'-bis[(1E)-3-phenylprop-2-en-1-ylidene]hexane-1,6-diamine N,N'-bis[(1E,2E)-3-phenylprop-2-en-1-ylidene]hexane-1,6-diamine |
CAS | 140-73-8 |
EINECS | 205-429-9 |
InChI | InChI=1/C24H28N2/c1(9-19-25-21-11-17-23-13-5-3-6-14-23)2-10-20-26-22-12-18-24-15-7-4-8-16-24/h3-8,11-18,21-22H,1-2,9-10,19-20H2/b17-11+,18-12+,25-21+,26-22+ |
Molecular Formula | C24H28N2 |
Molar Mass | 344.49 |
Density | 0.92±0.1 g/cm3(Predicted) |
Boling Point | 530.5±50.0 °C(Predicted) |
Flash Point | 267.8°C |
Water Solubility | 44mg/L at 25℃ |
Vapor Presure | 0Pa at 25℃ |
pKa | 7.05±0.50(Predicted) |
Storage Condition | 2-8°C |
Refractive Index | 1.527 |
MDL | MFCD00046784 |
LogP | 1.87 at 25℃ |
EPA chemical information | Information provided by: ofmpub.epa.gov (external link) |
use | as a vulcanizing agent for fluororubber, it has excellent vulcanization performance and can avoid pores in vulcanized rubber. 2-3 parts in carbon black compound and 3-4 parts in mineral filler compound. Usually, the first stage of molding at 149 ℃ is used for 30 minutes and the second stage of hot air vulcanization at 204 ℃ is used for 24 hours. |