丙烯酸乳液

丙烯酸乳液 - Names and Identifiers

Name	ACRYLIC EMULSION
Synonyms	Rhoplex E-358 ACRYLIC EMULSION polyacrylic emulsion

丙烯酸乳液 - Physico-chemical Properties

Use

Acrylic Emulsion is used as an adhesive, compared with other adhesives, it is particularly excellent in weather resistance and aging resistance, and has high adhesive strength, good water resistance, large elasticity and high elongation at break. Therefore, it is widely used in pressure sensitive adhesives, fabric printing and dyeing adhesive, electrostatic adhesive, paper glue, etc.

丙烯酸乳液 - Overview

polyacrylic acid-based copolymer emulsion. It is generally based on methyl acrylate and other acrylic acid low Ester organic compounds as the main monomer, and acrylonitrile, styrene, dibutyl maleate, methacrylate, vinyl chloride, vinylidene chloride or vinyl acetate copolymerization. Functional monomers, such as (meth) acrylic acid, maleic acid, fumaric acid, (meth) acrylamide, and the like, are sometimes introduced in order to impart certain specific properties to the polymer emulsion.

Last Update：2024-04-10 22:29:15

丙烯酸乳液 - Preparation

19.3 parts by weight of deionized water, 35.5 parts of isooctyl acrylate, 4.5 parts of methyl methacrylate, 1.1 parts of styrene, 2.3 parts of Hydroxyethyl acrylate, 3 parts of acrylic acid, 0.9 parts of vinyltriethoxysilane, dodecylmercaptan 0.06 parts, nonylphenol polyoxyethylene ether ammonium sulfate 0.2 parts, and α-thio-& omega;-[1-[(4-nonylphenoxy)] methyl]-2-(2-propenyl-1-oxy) ethoxy]-Poly (oxy-1, 2-ethanediyl) ammonium salt 0.13 parts, put into pre-emulsification tank for emulsification, after all raw materials are uniformly dispersed, stop stirring to form pre-emulsion;

supply 30 parts of deionized water, 0.2 parts of polyoxyethylene lauryl ether, and 0.1 parts of sodium bicarbonate into a four-necked flask equipped with a stirrer, thermometer, condenser, and burette, add 0.1 parts of ammonium persulfate and 2.2 parts by weight of pre-emulsion, heated to 77 deg C;

The remaining pre-emulsion and 0.1 parts of ammonium persulfate were titrated for 4.5 hours, and the temperature was maintained at 83~85 °c;

2.3 parts of methyl methacrylate was added dropwise for 30 minutes, and the temperature was maintained at 83~85 ℃; After the titration was finished, the temperature was maintained for 1.5 hours; Cooled to 60 ℃, 0.12 parts of white block and 0.09 parts of tert-butyl hydroperoxide were put in, incubation for 1 hour; Cooling discharge.

Last Update：2024-04-10 22:29:15

丙烯酸乳液 - Reference Information

Overview	polyacrylic copolymer emulsion. It is generally based on methyl acrylate and other acrylic acid low Ester organic compounds as the main monomer, and acrylonitrile, styrene, dibutyl maleate, methacrylate, vinyl chloride, vinylidene chloride or vinyl acetate copolymerization. Functional monomers, such as (meth) acrylic acid, maleic acid, fumaric acid, (meth) acrylamide, and the like, are sometimes introduced in order to impart certain specific properties to the polymer emulsion.
Application	acrylic emulsion is used as an adhesive, which is particularly excellent in weather resistance and aging resistance compared with other adhesives, and high adhesive strength, good water resistance, large elasticity, high elongation at break, so it is widely used in pressure sensitive adhesive, fabric printing and dyeing adhesive, electrostatic adhesive, paper adhesive.
preparation	19.3 parts by weight of deionized water, 35.5 parts of isooctyl acrylate, 4.5 parts of methyl methacrylate, 1.1 parts of styrene, hydroxyethyl acrylate 2.3 parts, acrylic acid 3 parts, vinyltriethoxysilane 0.9 parts, dodecylmercaptan 0.06 parts, nonylphenol polyoxyethylene ether ammonium sulfate 0.2 parts, and α-thio-ω-[1-[(4-nonylphenoxy) methyl]-2-(2-propenyl-1-oxy) ethoxy]-Poly (oxy -1, 2-ethanediyl) ammonium salt 0.13 parts, put into pre-emulsification tank for emulsification, after all raw materials are uniformly dispersed, stop stirring to form pre-emulsion; supply 30 parts of deionized water, 0.2 parts of polyoxyethylene lauryl ether, and 0.1 parts of sodium bicarbonate into a four-necked flask equipped with a stirrer, thermometer, condenser, and burette, add 0.1 parts of ammonium persulfate and 2.2 parts by weight of pre-emulsion, and heat to 77 ℃; Titrate the remaining pre-emulsion and 0.1 parts of ammonium persulfate for 4.5 hours, and maintain the temperature at 83~85 ℃; 2.3 parts of methyl methacrylate was added dropwise for 30 minutes, and the temperature was maintained at 83-85 ° C; after completion of the titration, the mixture was maintained for 1.5 hours; Cooled to 60 ° C., 0.12 parts of the white block and 0.09 parts of tert-butyl hydroperoxide were charged, and the mixture was maintained for 1 hour; And discharged by cooling.